Polycarbonate Films Spec. |
|||
|
Property |
Test Method |
Units |
Value |
|
Physical |
|||
|
Specific Gravity |
ASTM D792 |
G/cm3 |
1.2 |
|
Water Absorption Equilibrium,24Hrs |
ASTM D570 |
% |
0.35 |
|
|
|||
|
Tensile Strength |
ASTM D882 |
Psi |
8,800 |
|
ISO R1184-1987 |
Mpa |
60 |
|
|
Elongation Ultimate |
ASTM D882 |
% |
>90 |
|
Impact Strength @ 10mils |
JIS-k6745 |
In-ibs |
120 |
|
Tear Strength Propagation |
ASTM D1922 |
G/mil |
>30 |
|
Temperature Resistance |
|||
|
Vicat Softening Temperature |
ASTM D1525 |
℃ |
110 |
|
Heat Shrinkage Rate |
ASTM D1204 |
% |
<1.0 |
|
Electrical |
|||
|
Dielectric Strength (@ 10 mils) |
ASTM D149 |
V/mil |
1700 |
|
Volume Resistivity @25℃,50%RH |
ASTM D257 |
Ohm.m |
1016 |
|
Surface Resistivity @25℃,50%RH |
ASTM D257 |
Ohm |
1015 |
|
Flammability |
|||
|
UL 防火等级 UL Flammability |
UL BULLETIN94 |
|
|
|
@ ≥ 10 mils |
|
UL94 |
V0 |
|
@ ＜ 10 mils |
|
UL94 |
VTM-0 |
|
Property |
Unit |
Ultimate Value |
|
|
Gaute Variation |
% |
＞0.5 ±0.006mm |
|
|
≦0.5 ±0.004mm |