产品 |
定属名称 |
比重 (g/cm3) |
熔流率 (g/10 min) |
|
CALIBRE 1080 DVD |
聚碳酸酯 |
1.20 (ASTM D792); 1.20 (ISO 1183); 1.19 (ISO 1183) |
11 (250°C/1.2 kg, ASTM D1238); 11 (250°C/1.2 kg, ISO 1133) |
|
CALIBRE 200-10 |
聚碳酸酯 |
1.20 (ISO 1183); 1.20 (ISO 1183) |
10 (300°C/1.2 kg, ISO 1133) |
|
CALIBRE 200-15 |
聚碳酸酯 |
1.20 (ASTM D792); 1.20 (ISO 1183); 1.20 (ISO 1183) |
15 (300°C/1.2 kg, ASTM D1238); 15 (300°C/1.2 kg, ISO 1133) |
|
CALIBRE 200-22 |
聚碳酸酯 |
1.20 (ASTM D792); 1.20 (ISO 1183); 1.20 (ISO 1183) |
22 (300°C/1.2 kg, ASTM D1238); 22 (300°C/1.2 kg, ISO 1133) |
|
CALIBRE 200-3 |
聚碳酸酯 |
1.20 (ASTM D792); 1.20 (ISO 1183) |
3.0 (300°C/1.2 kg, ASTM D1238); 3.0 (300°C/1.2 kg, ISO 1133) |
|
CALIBRE 200-4 |
聚碳酸酯 |
1.20 (ASTM D792); 1.20 (ISO 1183); 1.20 (ISO 1183) |
4.0 (300°C/1.2 kg, ASTM D1238); 4.0 (300°C/1.2 kg, ISO 1133) |
|
CALIBRE 200-6 |
聚碳酸酯 |
1.20 (ASTM D792); 1.20 (ISO 1183); 1.20 (ISO 1183) |
6.0 (300°C/1.2 kg, ASTM D1238); 6.0 (300°C/1.2 kg, ISO 1133) |
|
CALIBRE 200-8 |
聚碳酸酯 |
1.20 (ISO 1183) |
8.0 (300°C/1.2 kg, ISO 1133) |
|
CALIBRE 201-10 |
聚碳酸酯 |
1.20 (ISO 1183); 1.20 (ISO 1183) |
10 (300°C/1.2 kg, ISO 1133) |
|
CALIBRE 201-15 |
聚碳酸酯 |
1.20 (ASTM D792); 1.20 (ISO 1183); 1.20 (ISO 1183) |
15 (300°C/1.2 kg, ASTM D1238); 15 (300°C/1.2 kg, ISO 1133) |
|
CALIBRE 201-18 |
聚碳酸酯 |
|
18 (300°C/1.2 kg, ASTM D1238) |
|
CALIBRE 201-22 |
聚碳酸酯 |
1.20 (ASTM D792); 1.20 (ISO 1183); 1.20 (ISO 1183) |
22 (300°C/1.2 kg, ASTM D1238); 22 (300°C/1.2 kg, ISO 1133) |
|
CALIBRE 201-5 |
聚碳酸酯 |
1.20 (ASTM D792) |
5.0 (300°C/1.2 kg, ASTM D1238) |
|
CALIBRE 201-6 |
聚碳酸酯 |
1.20 (ASTM D792); 1.20 (ISO 1183); 1.20 (ISO 1183) |
6.0 (300°C/1.2 kg, ASTM D1238); 6.0 (300°C/1.2 kg, ISO 1133) |
|
CALIBRE 201-8 |
聚碳酸酯 |
1.20 (ISO 1183) |
8.0 (300°C/1.2 kg, ISO 1133) |
|
CALIBRE 203-15 |
聚碳酸酯 |
1.20 (ASTM D792); 1.20 (ISO 1183); 1.20 (ISO 1183) |
15 (300°C/1.2 kg, ASTM D1238); 15 (300°C/1.2 kg, ISO 1133) |
|
CALIBRE 2060-6 |
聚碳酸酯 |
1.20 (ASTM D792); 1.20 (ISO 1183) |
6.0 (300°C/1.2 kg, ASTM D1238); 6.0 (300°C/1.2 kg, ISO 1133) |
|
|